Principal Properties & Application:
ALITA 901 resin is a bisphenol A type epoxy vinyl ester resin primarily composed of epoxy resin and methacrylic acid. It has moderate viscosity and reactivity. ALITA 901 resin falls into the category of Chemically Resistant (CEE) materials, exhibiting high mechanical strength and excellent corrosion resistance. It can withstand the corrosive effects of most acids, alkalis, and salt solutions at temperatures up to 100°C. It is suitable
for manufacturing various chemical equipment such as pipes, containers, and tanks that require resistance to acid, alkali, and salt corrosion. It is also used in the production of high-quality glass fiber reinforced plastic molds and other fiberglass products.
Technical Specifications of Liquid Resin:
| Project | Scope | Unit | Test Method |
| Exterior | yellow transparent viscous liquid | - | - |
| Acid Value | 9-15 | mgKOH/g | GB/T 2895-2008 |
| Viscosity, 25℃ | 0.4-0.5 | Pa.s | GB/T 7193-2008 |
| Solid Content | 55-61 | % | GB/T 7193-2008 |
| Thermal Stability, 80°C | ≥24 | h | GB/T 7193-2008 |
| Gelation Time, 25℃ | 20-30 | min | GB/T 7193-2008 |
Note: Gel Time Testing: A 25°C water bath was used, and 0.9g of catalyst (1% Co) and 0.9g of M-50 (Nouryon) were added to 50g of resin.
Casting Body Physical Properties (for reference only):
| Project | Typical Value | Unit | Test Method |
| Exterior | Casting without defects | - | - |
| Barcol hardness | 44 | - | GB/T 3854-2005 |
| Heat distortion temperature | 110 | ℃ | GB/T 1634-2004 |
| Elongation at break | 3.0 | % | GB/T 2567-2008 |
| Tensile Strength | 70 | Mpa | GB/T 2567-2008 |
| Tensile modulus | 3300 | Mpa | GB/T 2567-2008 |
| Bending strength | 120 | Mpa | GB/T 2567-2008 |
| Flexural modulus of elasticity | 3500 | Mpa | GB/T 2567-2008 |
Note: The casting body fabrication method shall be executed according to Q/320411 BES002-2014.
Usage instructions:
1. ALITA 901 resin does not contain paraffin, accelerators, or thixotropic agents.
2. Recommended curing systems: pure cobalt-based accelerator 0.5-4.0%, MEKP curing agent 1-3%; for harsh construction environments (such as low temperature, high humidity), recommended 10% DMA (dimethylaniline) liquid 0.5-2.0%, 50% BPO (benzoyl peroxide) paste 2-4%. In actual operation, the dosage of curing agent and accelerator should be determined based on environmental conditions such as temperature
and humidity through on-site testing.
3. When selecting heat-resistant and chemically resistant corrosion protection resins, the choice should be based on the actual usage medium and temperature of the product, referring to our company's "Heat-Resistant and Chemically Resistant Medium Usage Query Table" to select the appropriate resin, and confirm it through tests.
4. Curing is particularly important after corrosion-resistant fiberglass reinforced plastic products are made. The products should be used only after they have fully cured.
Handling and Storage:
This resin contains ingredients which could be harmful if mishandled. Contact with skin and eyes should be avoided and necessary protective equipment and clothing should be worn.
Drums - It is highly recommended that all material is stored at stable temperatures below 25°C (77°F). Avoid exposure to heat sources such as direct sunlight or steam pipes. To avoid contamination of product with water, do not store outdoors. Keep sealed to prevent moisture pick-up and monomer loss. Rotate stock.