ALITA 1506 Unsaturated Polyester Resin - High Viscosity & Reactivity

Principal Properties & Application:

ALITA 1506 resin is a new pentanediol-based unsaturated polyester resin primarily derived from phthalic anhydride and neopentyl glycol. It has high viscosity and high reactivity. ALITA 1506 resin thickens quickly, has good flowability, and exhibits excellent strength and toughness. It is suitable for general SMC/BMC products.

Liquid resin technical indicators:

Item	Scope	Unit	Test Method
Exterior	light yellow transparent liquid	-	-
acid value	17-25	mgKOH/g	GB/T 2895-2008
Viscosity, 25℃	1.2-1.8	Pa.s	GB/T 7193-2008
solid content	64-70	%	GB/T 7193-2008
SPI-GT(80℃)	5-10	min	ALITA-D-DB001

Note: When testing the cure performance of SPI (Structural Polyurethane Injection) system, the curing agent used is Enox BPO-50F with a dosage of 2%.

Physical properties of the casting (for reference only):

Item	Typical Value	Unit	Test Method
Exterior	Casting without defects	-	-
Barcol hardness	45	-	GB/T 3854-2005
Heat distortion temperature	75	℃	GB/T 1634-2004
Elongation at break	2.5	%	GB/T 2567-2008
Tensile Strength	68	Mpa	GB/T 2567-2008
Tensile modulus	3150	Mpa	GB/T 2567-2008
Bending strength	125	Mpa	GB/T 2567-2008
Flexural modulus of elasticity	3750	Mpa	GB/T 2567-2008

Note:
The casting fabrication method is conducted in accordance with GB/T 8237-2005. The curing system consists of a promoter (0.6% Co Naph) and a curing agent (Butanox M-50: 1.0%).
The post-casting treatment involves subjecting the castings to room temperature for 24 hours, followed by heating at 60°C for 3 hours, and finally at 120°C for 1 hour.

Usage instructions:

ALITA 1506 resin does not contain wax, promoters, or thixotropic agents.
To ensure the storage stability of SMC/BMC materials, stabilizers should be added appropriately during production.

Handling and Storage:

This resin contains ingredients which could be harmful if mishandled. Contact with skin and eyes should be avoided and necessary protective equipment and clothing should be worn.
Drums - It is highly recommended that all material is stored at stable temperatures below 25°C (77°F). Avoid exposure to heat sources such as direct sunlight or steam pipes. To avoid contamination of product with water, do not store outdoors. Keep sealed to prevent moisture pick-up and monomer loss. Rotate stock.

At Alita, we proudly uphold a global service commitment, ensuring a seamless experience for our international clients. Our offerings include flexible supply chain management, comprehensive global logistics support, and tailor-made solutions. We want our customers to be confident in our ability to navigate international trade successfully. With our dedication to excellence, we stand ready to provide unparalleled service and address the unique needs of clients worldwide.

chen cheng

ALITA PS-9045C Low Profile (LP) Additive

Principal Properties & Application: ALITA PS-9045C unsaturated polyester resin is used as a low-shrinkage additive for SMC/BMC applications, offering excellent colorability. It is compatible with unsaturated polyester resins and is suitable for general-purpose SMC/BMC products in electrical, industrial, residential, and automotive applications. Specifications of Liquid Resin: Item Specification Test Method Appearance Slightly cloudy white liquid

2025-03-19 No Comments

p-Benzoquinone (PBQ) Polymerization Inhibitor – 10% PBQ Solution

Overview p-Benzoquinone (PBQ) is a highly effective polymerization inhibitor widely used in various chemical processes. Its superior thermal stability and inhibition efficiency make it an excellent choice for preventing premature polymerization in monomers such as styrene, vinyl acetate, methyl methacrylate, and unsaturated polyester resins. This 10% PBQ solution is formulated for easy application and enhanced

2025-03-12 No Comments

Enox® BIBP Di(tert-butylperoxyisopropyl)benzene 25155-25-3

Enox BlBP is a white to yellowish solid. It is used for the crosslinking of natural rubber, synthetic rubbers, and polyolefins. CAS-No 25155-25-3 CH₃ CH₃ CH₃ CH₃ | | | | CH₃ - C - O - O - C - ⬡ - C - O - O - C - CH₃ | | |

2024-11-06 No Comments

Enox® PMBP Di(4-methylbenzoyl) peroxide 895-85-2

Enox PMBP is a diacyl peroxide crosslinking agent for silicone rubber. Using Enox DCBP, blooming is not often observed, along with problems such as excess chloride and hazardous decomposition products. CAS-No 895-85-2 O O ∥ ∥ H₃C - ⬡ - C - O - O - C - ⬡ - CH₃ C₁₆H₁₄O₄=270.28 Safety DataSADT: 80℃UN-No.:

2024-11-06 No Comments

Enox® TMCH-40DB 1,1-Di-(tert-butylperoxy)-3,3,5-trimethylcyclohexane 6731-36-8

Enox TMCH-40DB is a white powder. It is used for crosslinking silicone rubbers. CAS-No 6731-36-8 CH₃ CH₃ | | H₃C - C - O - O O - O - C - CH₃ | / | CH₃ / CH₃ / H₃C CH₃ CH₃ C₁₇H₃₄O₄=302.46 Safety DataFlash Point(Shut): 60℃UN-No.(90%): 3110CN-No.: 52011PropertiesAppearance: SolidDensity: 0.41~0.45Theoretical Active Oxygen: 10.58%SpecificationAppearance:

2024-11-06 No Comments

Enox® 101-60D-pd Powder 2,5-Dimethyl-2,5-di(tert-butylperoxy)hexane 78-63-7 DHBP

Enox 101-60D-PD is a white powder. It is used for crosslinking silicone rubbers.CAS-No 78-63-7 CH₃ CH₃ CH₃ CH₃ | | | | CH₃ - C - O - O - C - CH₂ - CH₂- C - O - O - C - CH₃ | | | | CH₃ CH₃ CH₃ CH₃ C₁₆H₃₄O₄=290.44 Safety DataFlash

2024-11-06 No Comments

Product Consultation

Scheduling An Appointment

Please let us know if you have any questions!